1. V-0 Fire Rating: UL94 V-0 certified, reducing fire risk in sealed or high-density power assemblies.
2. Flexible Curing: Pot life 20–60 min; cures in 6–9 h at 25°C (adjustable) or ≤60 min at 60°C for high-volume throughput.
3. Strong Insulation: Breakdown voltage ≥15 kV/mm; surface resistivity ≥1.0×10¹¹ Ω/sq for secure component isolation.
4. Mechanical Toughness: Shore A 70±10, tensile ≥2 MPa – absorbs shock and accommodates thermal movement.
5. Color Options: Available in black, white, or beige to meet design and functional needs.
6. Global Compliance: Meets RoHS, REACH, and UL94 V-0, aligning with international automotive and electronics standards..
|
Parameters |
Hardener BZ-6806-2R A |
Resin BZ-6806-2R B |
||
|
Before curing |
Appearance |
Brown liquid |
Black/White/Beige liquid |
|
|
Viscosity(mPa·s.25℃) |
100±40 |
16500±5000 |
||
|
Initial mixed viscosity(mPa·s.25℃) |
1600±500 |
|||
|
Density(g/cm³.25℃) |
1.07±0.05 |
1.54±0.05 |
||
|
Mixing & Curing
|
Mix ratio(by weight) |
A:B=30:100 |
||
|
Pot life 130±30g(min.25℃) |
20-60 (Adjustable for process/temperature ) |
|||
|
Curing condition |
Room temperature curing |
|||
|
Surface drying time 30g(H.25℃) |
3-6.5 (Adjustable for process/temperature ) |
|||
|
Curing time 30g(H.25℃) |
6-9 (Adjustable for process/temperature ) |
|||
|
Curing time(Heated) |
60℃ heated ≤60 min |
|||
|
After curing
|
Color |
Black/White/Beige |
||
|
Hardness (Shore A) |
70±5 |
|||
|
Temperature resistance(℃) |
-40~120℃ |
|||
|
Flame retardancy UL94
|
V0 |
|||
|
Thermal conductivity(W/m.k) |
≥0.40 |
|||
|
Water absorption(24H) |
≤0.5% |
|||
|
Surface resistivity(Ω/sq) |
≥1.0×1011 |
|||
|
Volume resistivity(Ω.cm) |
≥1.0×1010 |
|||
|
Tensile strength(MPa) |
≥2 |
|||
|
Dielectric constant(at 50Hz) |
≥4 |
|||
|
Breakdown voltage(kV/mm) |
≥15 |
|||